It is created from electrical glass cloth with alkali-free that has been impregnated with diphenyl ether resin under pressure. Heat and rolling. The thermal grade is class H insulation. With excellent mechanical strength and dielectric property after in wet, self-extinguish, radiation-proof. Used for the insulating slots. windings. gaskets. junction boards of the dry-type transformer/mine transformer/motor/electrical equipment which are working at high temperature.
melamine glass cloth laminated, diphenyl ether glass cloth laminated
Sheets: Thickness 0.5-200mm Size:1000X2000mm
technical data
No Specification Unit Index
1 Water absorption % <= 0.5
2 Martin temperature oC >= 250
3 Flexural strength, lengthwise Mpa >= 343
4 Tensile strength, lengthwise Mpa >= 294
5 Bonding strength N >= 5688
6 Impact strength, lengthwise KJ/ M2 >= 147
7 Surface resistively At room temperature >= 10 5
After wet M Ω >= 10 3
At room temperature >= 10 5
8 Volume resistively After wet M Ω m >= 10 3
180 oC >= 10 2
Electrical strength 0.5-1mm >= 22
9 perpendicular to lamination 1.2-2mm MV/m >= 20
in transformer oil at 90 oC 2.1-3mm >= 18
Above 3mm >= 18
10 Breakdown voltage parallel to lamination KV >= 22
melamine glass cloth laminated, diphenyl ether glass cloth laminated | 